US$3.50 | 1 kg (MOQ) |
Liner density | Density | No. of Filament | Breaking Tenacity | Elongation at Break | Hot air Shrinkage(10 min,177ºC) | Boiling water shrinkage (30 min) | |
Dtex | Denier | F | G/D | CN/dtex | % | % | % |
33 | 30 | 12 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
45 | 40 | 18 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
56 | 50 | 24 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
61 | 55 | 24 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
78 | 70 | 30 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
95 | 85 | 30 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
111 | 100 | 36 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
125 | 112 | 36 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
133 | 120 | 36 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
140 | 126 | 48 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
167 | 150 | 48 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
233 | 210 | 72 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
278 | 250 | 72 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
333 | 200 | 96 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |
467 | 420 | 144 | 8.2±0.2 | 7.24±0.2 | 13.5±0.5 | 1.8±0.5 | 1.5±0.3 |